利用热磺化工艺和热处理工艺将废弃的涤纶面料转变成硬碳并作为负极材料,制备了锂离子电池。通过热重分析仪、X射线衍射仪和扫描电子显微镜等分析手段证实了涤纶面料变成了非晶态硬碳材料。热磺化工艺将聚酯(PET)链上的部分H原子转化为磺酸基(SO3H)基团,热处理工艺将大部分杂质去除以生成大孔隙的碳。采用恒流充放电法对组装的锂离子电池进行测试,在0.1A/g的电流密度下,电池首次比容量达到437mAh/g,循环50次后,比容量保持在220mAh/g左右。利用废弃涤纶面料制备的锂离子电池负极材料电化学性能良好且制作成本低,为废弃聚酯回收再利用提供了新的思路。
The waste polyester fabric was converted into hard carbon by thermosulfonation and heat treatment to prepare lithium-ion battery.Thermogravimetric analyzer,X-ray diffractometer and scanning electron microscope were used to confirm that the polyester fabric had become an amorphous hard carbon material.The thermosulfonation process converted some H atoms in the PET chain to SO3H(sulfonic acid) groups,and the heat treatment process removed most of the impurities to form large pores of carbon.Constant current charging-discharge method was used to test the assembled lithium-ion battery.Under the current density of 0.1A/g,its first specific capacity reached 437mAh/g.After 50 cycles,the specific capacity remained about 220mAh/g.The cathode material for lithium-ion battery prepared from waste polyester fabric had good electrochemical performance and low production cost,which provided a new idea for recycling waste polyester.
[1] 詹发林.涤纶聚酯降解及回收利用探讨[J].轻纺工业与技术,2019,48(6):59-65.
[2] 吕亚淑,余天石,郑佳,等.回收利用涤纶中试醇解废液再降解聚酯PET[J].功能材料,2016,47(2):2258-2262.
[3] 王春梅,赵海雷,王静,等.锂离子电池硬碳负极材料的制备及性能表征[J].电源技术,2013,37(11):1932-1935.
[4] 唐致远,庄新国,翟玉梅,等.锂离子电池酚醛树脂裂解碳负极材料的研究[J].电化学,2000(2):218-221.
[5] 李艳红,吴锋,吴川,等.锂离子电池负极用Sb一活性炭复合材料的制备及其性能表征[J].过程工程学报,2008,8(5):993-997.
[6] 李玉龙,刘瑞峰,周颖,等.锂离子电池硬碳负极材料的研究进展[J].材料导报,2017,31(29):236-241.
[7] 谢朝香.锂离子电池碳负极材料的研究[D].哈尔滨:哈尔滨工业大学,2010.
[8] 金娟.聚丙烯腈基硬碳的制备及其储锂/钠性能的研究[D].天津:天津大学,2015.
[9] 范长岭,徐仲榆.乙炔黑在锂离子电池负极中的贮锂功能[J].炭素技术,2007(1):19-21.
[10] 郭红祥.由稻壳制备锂离子电池硅/碳复合负极材料[D].南昌:南昌大学,2017.
[11] 肖钰,刘慕函,廖丽霞,等.基于稻谷壳的多孔生物质碳锂离子电池负极材料的制备及性能研究[J].化工新型材料,2019,47(12):113-116.
[12] Saul V S,Palanisamy M,Salvador F A G,et al.Amorphous carbon chips Li-ion battery anodes produced through polyethylene waste upcycling[J].ACS Omega,2018,3(12):17520-17527.
[13] 费雅倩.铁酸锌复合纳米纤维材料的制备和电化学性能研究[D].无锡:江南大学,2017,
[14] Vinodkumar E,Chulgi N H,Vilus G P,et al.Toward high-performance lithium-sulfur batteries:upcycling of LDPE plastic into sulfonated carbon scaffold via microwave-promoted sulfonation[J].ACS Applied Materials & Interfaces,2018,10(17):14827-14834.
[15] 林雪,王成国,于美杰,等.基于XRD的径向分布函数法研究碳纤维制备过程中的结构演变[J].航空材料学报,2013,33(1):72-77.
[16] 李同起,杨晓光,许正辉,等.样品位置对碳材料XRD测试结果的影响[J].宇航材料工艺,2009,39(4):76-80.
[17] 高小转.葡萄糖水热碳化制备多孔碳电极材料及改性研究[D].太原:太原理工大学,2018.
[18] 王素卿,张学军,田艳红,等.碳纤维制品结构分析及其用作锂离子电池负极材料性能研究[J].高科技纤维与应用,2012,37(6):25-29.
[19] 陈逸民.锂离子电池纳米复合碳负极材料的研究[D].上海:复旦大学,2009.
[20] 刘文刚,周波,王晓丹,等.18650型锂离子电池的循环容量衰减研究[J].电源技术,2012,36(3):306-309.
基金资助
国家自然科学基金青年基金(51903107);江苏省自然科学基金青年基金(BK20190619);中国博士后面上资助项目(2019M661724);江苏省博士后基金科研资助项目(2019K107);中国化学纤维工业协会绿宇基金资助项目(CCFA-LVYU-2019-03),江南大学大学生创新训练计划(2020542X)
PDF